Chemical analysis of n-propyl gallate used as pre-treatment for resin-dentin bond strength: In vitro study.

This study aimed to evaluate the effect of n-propyl gallate as pre-treatment for resin-dentin bond strength. The dentin pre-treatments evaluated included propyl gallate of concentrations 0.1% (w/v), 1.0% (w/v), and 10.0% (w/v), as well as glutaraldehyde 5.0% (v/v), and distilled water as a control treatment. Dentin specimens were prepared for Fourier Transformed Infrared Spectroscopy (FT-IR) (n = 3/pre-treatment). Pre-treatments were actively applied to dentin blocks before performing the adhesive procedure to composite resin. Microtensile bond strength to dentin (µTBS) (n = 8/pre-treatment) was determined after 24 h and 6 months of storage. Data were submitted to a two-way ANOVA, followed by Tukey's post hoc test. As for FT-IR, propyl gallate 1%-treated specimens presented higher water, carbonate, collagen, and amide absorbance rates compared to other tested groups, while specimens pre-treated with glutaraldehyde and distilled water presented similar absorbance curves. Regarding µTBS, all concentrations of propyl gallate resulted in statistically significant higher bond strength values than distilled water at 24 h. After 6 months of storage, propyl gallate 0.1% was the only group that maintained µTBS over time. Propyl gallate 0.1% might be a suitable dentinal pre-treatment due to being able to present chemical bonds with demineralized dentin and providing resin-dentin bond stability after 6 months of storage.

Efeito Biomodificador de Diferentes Agentes de Ligações Cruzadas nas Propriedades Mecânicas do Colágeno Dentinário / Biomodifying Effect of Different Cross-Linking Agents on the Mechanical Properties of Dentin Collagen

Objetivo: avaliar o efeito biomodificador dos agentes de ligações cruzadas nas propriedades mecânicas do colágeno dentinário. Material e Métodos: Trata-se de um estudo laboratorial in vitro, nos quais foram confeccionadas 18 barras de dentina a partir de terceiros molares humanos extraídos e livres de cárie. Os espécimes foram desmineralizados em ácido fosfórico a 10%, por 5 horas, distribuídos aleatoriamente nos grupos distintos e mantidos em suas respectivas soluções de pré-tratamento: água destilada (AD), Proantocianidina a 6,5% (PAC6,5) e Cardanol a 6,5% (CAR6,5) por períodos de 1 hora. Foram realizados os testes de flexão de três pontos para obtenção do módulo de elasticidade (ME) e modificação de massa (MM). Foram submetidos ao teste de Kolmogorov-Smirnoff seguido, do teste de ANOVA à um critério e pós teste de Tukey para a MM, e Dunns para diferença de ME (p<0,05). Resultados: Os valores obtidos no ME mostraram mudanças estatísticas notáveis em todos os grupos testados, quando comparados ao controle negativo (p<0,001), assim como na variação de massa foram encontradas diferenças estatísticas nos valores médios entre os grupos testados (p=0,012). Conclusão: o uso da PAC6,5 irá melhorar as propriedades mecânicas do colágeno

Objective: to evaluate the biomodifying effect of cross-linking agents on the mechanical properties of the teeth. Material and Methods: this is an in vitro laboratory study, in which 18 bars of dentin were made from extracted, caries-free human third molars. The samples were demineralized in 10% phosphoric acid for 5 hours, randomly distributed in different groups and kept in their pre-treatment solutions: distilled water (AD), Proanthocyanidin at 6.5% (PAC6.5) and Cardanol at 6.5% (CAR6.5) for periods of 1 hour. Three-point bending tests were performed to obtain the modulus of elasticity (ME) and mass modification (MM). They were submitted to the Kolmogorov-Smirnoff test followed by the Kruskal-Wallis' test and the Tukey's post-test for mass modification, and Kruskal-Wallis' test after a Dunn's test for difference in the modulus of elasticity(p <0.05). Results: the values selected in the ME show possible statistical changes in all groups tested, when compared to the negative control (p<0.001), as well as the mass variation. Data were shown in the average values between the groups tested (p = 0.012). Conclusion: The use of PAC6.5 will improve the mechanical properties of the collection

Correlação de Ansiedade com a Presença de Lesões Cervicais Dentárias não Cariosas / Association between anxiety and the presence of non-carious dental cervical lesions

Objetivo: este estudo tem como objetivo avaliar a associação entre ansiedade, hábitos alimentares, parafuncionais, condições sistêmicas, hábitos de higiene oral em associação com a ansiedade de pacientes com lesões cervicais dentárias não cariosas (LCNCs) em uma população. Material e Métodos: por meio de um estudo quantitativo, observacional, 100 pacientes, obtidos por cálculo do tamanho da amostra, com presença de LCNCs, foram avaliados por exame clínico e cálculo amostral; entre 20 e 58 anos, com idade média de 37 anos. Os dados foram coletados por meio de um questionário elaborado por um pesquisador previamente calibrado, referente à avaliação médica, odontológica, de histórico social e de ansiedade. Após a obtenção dos dados, eles foram tabulados e submetidos à análise estatística pelo teste binomial exato de Fisher de duas proporções, adotando um nível de significância de 5%. Resultados: o consumo de bebida gaseificada (81,6%), frutas cítricas (76,3%), frequência de escovação dentária igual ou superior a três vezes ao dia (100%) e abrasividade do creme dental (100%) foram significativamente associados à presença de NCCL (p = 0,0001). Doença do refluxo gastrointestinal, xerostomia, bulimia e anorexia demonstraram associação negativa com o NCCL (p=1,000). A ansiedade não mostrou relação direta com a NCCL na população estudada (36,8%). Conclusão: assim, pode-se concluir que não houve associação direta entre a presença de lesões cervicais não cariosas e a ansiedade

Objective: This study evaluated the association between parafunctional anxiety, eating habits, systemic conditions and assessment of oral hygiene habits with dental non-carious cervical lesions (NCCL). Material and Methods: this quantitative, observational study included 100 patients between 20 and 58 years old (mean of 37 years) with NCCL evaluated by clinical examination and sample calculation. The data were collected with use of a questionnaire made by a previously calibrated researcher, which referred to medical, dental, social history and anxiety assessments. After obtaining the data they were tabulated and subjected to statistical analysis using Fisher's exact two-proportion binomial test, adopting a 5% significance level. Results: consumption of carbonated drinks (81.6%), citrus fruits (76.3%), tooth brushing frequency equal or higher than three times a day (100%) and abrasiveness of toothpaste (100%) were significantly associated with presence of NCCL (p=0.0001). Gastrointestinal reflux, xerostomia, bulimia and anorexia showed negative association with NCCL (p=1.000). Anxiety was not directly associated with NCCL in the study population (36.8%). Conclusion: there was no direct association between the presence of non-carious cervical lesions and anxiety

Ácido tânico como agente biomodificador de dentina / Tanic acid as biomodificator of collagen dentin

Introdução: a utilização de diferentes polifenóis no aumento das propriedades mecânicas do colágeno dentinário tem sido bastante empregada, sendo o ácido tânico um polifenol com propriedade biológica bastante pronunciada. Objetivo: avaliar o potencial biomodificador do ácido tânico (AT) em diferentes concentrações em colágeno dentinário. Métodos: os fatores sob investigação foram módulo de elasticidade, mensurado por meio de um ensaio de flexão de três pontos (n=10) e variação de massa (n=10), aferidos com uma balança de precisão, sendo, para tanto, avaliados os seguintes elementos: ácido tânico (0,1; 1 e 10%), proantocianidina (6,5%) e água destilada (controle). Resultados: quanto ao módulo de elasticidade, os grupos tratados com ácido tânico apresentaram valores, estatisticamente, superiores (p<0,05) aos demais grupos, não sendo observadas diferenças entre suas diferentes concentrações. Para os valores de variação de massa, os grupos que foram imersos em agentes biomodificadores apresentaram valores estatisticamente (p<0,05) superiores ao grupo controle. Conclusão: o ácido tânico se apresenta como um potencial agente biomodificador do colágeno dentinário, independente da concentração utilizada, aumentando o seu módulo de elasticidade e gerando um ganho de massa após uma hora de imersão.

Introduction: The use of different polyphenols in the increase of the mechanical properties of dentin collagen has been widely used, thus, tannic acid being a polyphenol with very pronounced biological proprieties. Objective: to evaluate the biomodifying potential of tannic acid (AT) in different concentrations in dentin collagen. Methods: the factors under investigation were modulus of elasticity, measured by a three-point bending test (n = 10), and mass variation (n = 10), measured by means of a precision scale, being the following substances evaluated: tannic acid (0.1, 1 and 10%), proanthocyanidin (6.5%) and distilled water (control). Results: As for the modulus of elasticity, the groups treated with tannic acid presented statistically higher values (p <0.05) in relation to the other groups, and no differences were observed between the different concentrations. For the values of mass variation, the groups that were immersed in biomodifiers showed statistically (p <0.05) values higher than the control group. Conclusion: tannic acid presents as a potential biomodifying agent of dentin collagen, regardless of the concentration used, increasing its modulus of elasticity and generating a mass gain after one hour of immersion.

Avaliação do efeito de técnicas de acabamento e polimento na rugosidade superficial de resinas compostas / Evaluation of the effect of finishing and polishing techniques on surface roughness of composite resins

Introdução: o acabamento e o polimento das resinas compostas (RC) podem interferir diretamente na rugosidade desses materiais, estando relacionadas com a adesividade de placa bacteriana, manchamento, brilho e lisura. Objetivo: comparar a rugosidade superficial de duas RC, sendo uma micro-híbrida (Filtek Z250) e outra nanoparticulada (Filtek Z350), após a realização dos procedimentos de acabamento e polimento. Métodos: utilizando-se uma matriz metálica, confeccionaram-se quinze discos de cada RC. A lisura superficial proporcionada pela fita de poliéster foi avaliada por meio de um rugosímetro (Hommel Tech-T1000), obtendo-se dados iniciais. Realizou-se a mensuração em triplicata, obtendo-se o valor da rugosidade média (Ra). Lixaram-se as superfícies de topo dos espécimes e seguiu-se nova obtenção da Ra. Os espécimes foram, aleatoriamente, distribuídos em três grupos: GI ­ discos de óxido de alumínio; GII ­ pontas siliconadas e GIII ­ discos de diamante micronizado, sendo obtida a Ra final. Os dados foram analisados pelo teste de Kruskal-Wallis e Qui-quadrado (α=1%). Resultados: a média e o desvio-padrão expresso em µm foram: Z-250 GI - 0,16 (0,09), GII - 0,32 (0,06) e GIII - 0,06 (0,02) e para Z-350 GI - 0,06 (0,01), GII - 0,49 (0,14) e GIII - 0,07 (0,01). Para Z-250, o GIII apresentou melhor polimento, sendo, estatisticamente, diferente de GI e GII (p≤0,01). Para Z-350, não houve diferença estatística entre os GI e GIII, mas eles foram superiores ao GII (p≤0,01). Conclusão: o disco de diamante micronizado proporcionou melhores valores de lisura superficial independente do tipo de resina composta empregada.

Introduction: finishing and polishing of composite resins (CR) can directly interfere with the roughness of these materials, being related to bacterial plaque adhesion, staining, gloss and smoothness. Objective: to compare the surface roughness of two CR, a micro-hybrid (Filtek Z250) and a nanoparticulate (Filtek Z350) after finishing and polishing. Methods: using a metal matrix, fifteen disks of each CR were made. The surface smoothness provided by the polyester tape was evaluated by a rugosimeter (Hommel Tech-T1000) obtaining initial data. Measurements were made in triplicate, and the mean roughness value (Ra) was obtained. The top surfaces of the specimens were sieved and re-obtained the Ra. The specimens were randomly distributed into three groups: GI - aluminum oxide discs; GII - silicone tips and GIII - micronized diamond discs, obtaining the final Ra. Data were analyzed by the Kruskal-Wallis test and chi-square test (α = 1%). Results: the mean and standard deviation expressed in µm were: Z-250 GI - 0.16 (0.09), GII - 0.32 (0.06) and GIII - 0.06 (0.02) and for Z -350 GI - 0.06 (0.01), GII - 0.49 (0.14) and GIII - 0.07 (0.01). For Z-250, the GIII presented better polishing, being statistically different from GI and GII (p≤0.01). For Z-350, there was no statistical difference between GI and GIII, but these were higher than GII (p≤0.01). Conclusion: the micronized diamond disk provided better surface smoothness values independent on the type of composite resin used.

Dentin bonding and physicochemical properties of adhesives incorporated with epigallocatechin-3-gallate.

The aim was to assess dentin adhesion and physicochemical properties of experimental etch-and-rinse and self-etch adhesives doped with epigallocatechin-3-gallate (EGCG), a well-known collagen crosslinker obtained from green tea (Camellia sinensis). Experimental adhesives were prepared without (0 wt%), with 0.1 or 0.5 wt% EGCG addition. Their degree of conversion was surveyed by FTIR, and bar-shaped specimens were tested to obtain flexural strength and modulus initially and after 1-week ethanol storage. Extracted human molars were prepared, bonded, and cut into resin-dentin sticks for microtensile bond strength test, which was conducted after 24 h or 6-month water storage. Statistical analyses were performed with two-way ANOVA and Tukey's test (p < 0.05). Degree of conversion outcomes depicted a significant polymerization reduction by the addition of EGCG in self-etch adhesive in both concentrations. However, only 0.1% reduced the conversion of etch-and-rinse adhesive. Flexural modulus and strength were significantly diminished (p < 0.05) by the addition of both concentrations of EGCG for the two model adhesives. Dentin-bond strength was reduced after aging with the addition of EGCG to self-etch adhesive. Nevertheless, 0.5% EGCG increased the bond strength of etch-and-rinse adhesive after aging, conversely to the significant reduction for EGCG-free control adhesive. In conclusion, EGCG at 0.5% provides optimal improvements on dentin bonding without altering final polymerization of a model etch-and-rinse adhesive.

Efeito de diferentes agentes naturais biomodificadores na adesão à dentina hígida e afetada por cárie

A Odontologia restauradora minimamente invasiva tem priorizado cavidades mais conservadoras. Por isso o uso de estratégias como a biomodificação da dentina com o intuito de melhorar as propriedades mecânicas da camada híbrida e de proteger as fibrilas colágenas da degradação, tem ganhado cada vez mais destaque. O presente estudo tem o objetivo de avaliar a influência de diferentes agentes naturais de biomodificação sobre a resistência de união (RU) resina dentina, nanoinfiltração e micropermeabilidade em dentina hígida e afetada porcárie. Os fatores sob investigação são (1) pré-tratamento dentinário: álcool absoluto(controle negativo), pro antocianidinas a 2%; cardanol-metacrilato a 2%, cardol a 2%,cardol-metacrilato a 2% e epigalocatequina-3-galato (EGCG) a 0,1%; (2) tipo desubstrato dentinário: dentina hígida e dentina afetada por cárie artificialmente.Microtração (n=6), micropermeabilidade dentinária (n=3) e nanoinfiltração interfacial(n=6), foram avaliados em uma máquina de ensaios universais, microscopia confocala laser e microscopia eletrônica de varredura, respectivamente. Os valores de RUem dentina hígida foram superiores nos grupos tratados com cardol-metacrilato eEGCG. Já em dentina afetada por cárie, o grupo pré-tratado com cardol-metacrilatoapresentou resultados superiores aos demais grupos...

Minimally invasive dentistry has been prioritizing more conservative cavitypreparations. For this reason, the employment of strategies as dentin biomodification,to ameliorate the mechanical properties of resin-dentin interface and to protectcollagen fibrils from biodegradation, is highlighted as a promising technique. Thepresent study aimed to evaluate the influence of different natural biomodificationagents on resin-dentin bond strength, nanoleakage and micropermeability at soundand caries-affected dentin. The variable investigated were (1) dentin pre-treatment:absolute ethanol (control), proanthocyanidins (PACs) 2%, cardol (from cashew nutshell liquid) 2%, cardol-methacrylate 2%, cardanol-methacrylate 2% andepigallocatechin-3-gallate (EGCG) 0.1%; and (2) dentin substrate: sound dentin andartificial caries-affected dentin. Microtensile bond strength (n=6), dentinmicropermeability (n=3) and interfacial nanoleakage (n=6) were assessed on auniversal testing machine, confocal-laser scanning microscope and scanningelectron microscope respectively. The bond strength on sound dentin was higher byusing cardol-methacrylate and EGCG. On caries-affected dentin, pre-treatment usingcardol-methacrylate achieved the highest bond strength...